Evaluation opportunities of SEM pictures by CAD software
DOI:
https://doi.org/10.32972/dms.2019.011Keywords:
SEM, NURBS, Additive Manufacturing, material investigation, material propertiesAbstract
Nowadays the different 3D printed components are often produced for direct use. In this case the components need to be mechanical designed, therefore the material properties must be well known. It is a fact that the printing parameters have a significant effect on the printing quality. The interference between the printing parameters and the mechanical solidity is well known however the reason for this phenomenon is not. For a deeper investigation a scanning electron microscope is needed. Our study is focused on the potential evaluation of results with the help of the CAD software.
References
Kovács N. K., Suplicz A., Kovács J. G. (2011). Gyors prototípusgyártás, mint újszerű fröccsöntő szerszámozási technológia. Műanyag- és gumiipari évkönyv, 9, pp. 45-53, 9 p.
Horváth, Á. M., Ficzere, P. (2015). Rapid prototyping in medical sciences. Production Engineering Archives/Archiwum InżYnierii Produkcji, 8, 3, pp. 28-31, 4 p.
Ficzere P., Kovács N. K., Szebényi G., Borbás L. (2019). Additív gyártástehnológiával előállított nagyrugalmasságú anyagok terhelhetőségi vizsgálata. GÉP, LXX, 1, p. 43.
Ficzere, P., Borbás, L. (2018). Experimental Investigation of the Shear Modulus in the Case of Pure Tensile Test. Transactions of Famena, 42, 1, pp. 27-36, 10 p. https://doi.org/10.21278/TOF.42103
Ficzere, P., Borbás, L. (2012). Method to reduce the independent constants of orthotrop materials in rapid prototyping. 11th Youth Symposium on Experimental Solid Mechanics, Brasov, Románia, pp. 129-135, 7 p.
Tisza M., Tóth D., Kovács P. Z. (2016). A 3D nyomtatás (FDM) paramétereinek vizsgálata, optimalizálása. GÉP, 67, 1-2, pp. 29-32, 4 p.
Ficzere P., Borbás L., Falk Gy. (2018). Additív gyártástechnológiák alkalmazhatósági vizsgálata testreszabott orvosi implantátumok méretezéséhez. Biomechanica Hungarica, 11, 2, pp. 69-75, 7 p. https://doi.org/10.17489/2018/2/10